Vacuum Varying Pressure Nitriding Furnace
Delivery period
Vacuum varying pressure Nitriding furnace has been sold in 50 countries in the world, till now, we have manufactured 250 sets.
Vacuum varying pressure nitriding furnace delivery period is 45 days, supplier will provide all the relevant parts. Customer only needs to provide power and high purity ammonia.
Local installation is 10 days.
Features
1. High penetrating rate: Heat holds 8-10 hours, penetrating layer is 0.14-0.18mm, and bright white layer is 0.006-0.01mm.
2. It has a high surface hardness of HV1,000-1,200
3. The vacuum varying pressure nitriding furnace offers big load capacity and low cost for heat-treatment. Low vacuum varying pressure technology is used in the nitriding process. Fresh air reaches every corner of the inner furnace tank and provides drastically increased load capacity. As the furnace has excellent sealing and heat-insulating properties, it can largely reduce the cost for treatment.
4. It features small surface friction coefficient
5. It has low brittleness.
6. It features a stable performance. With uniform and controllable atmosphere and temperature inside furnace, the vacuum varying pressure nitriding furnace ensures stable nitriding and good nitriding effect.
Technical Parameters
|
Model No. |
Rated Power (kw) |
Rated Temp. (℃) |
Chamber Size Dia. × Height (mm) |
Temp. Uniformity (℃) |
Limiting Vacuum (MPa) |
Heating-up Time (min.) |
Load Capacity (kg) |
Furnace Weight (ton) |
|
ALM-20I |
20 |
650 |
Ф400×550 |
≤±5 |
-0.08 |
≤80 |
160 |
1.6 |
|
ALM-30I |
30 |
650 |
Ф450×650 |
≤±5 |
-0.08 |
≤80 |
200 |
2.0 |
|
ALM-45I |
45 |
650 |
Ф550×1000 |
≤±5 |
-0.08 |
≤80 |
400 |
2.5 |
|
ALM-60I |
60 |
650 |
Ф650×1200 |
≤±5 |
-0.08 |
≤80 |
800 |
3.2 |
|
ALM-75I |
75 |
650 |
Ф800×1200 |
≤±5 |
-0.08 |
≤80 |
1200 |
3.5 |
|
ALM-90I |
90 |
650 |
Ф800×1800 |
≤±5 |
-0.08 |
≤80 |
1600 |
4.2 |
|
ALM-110I |
110 |
650 |
Ф800×2500 |
≤±5 |
-0.08 |
≤80 |
2200 |
5.0 |
|
ALM-140I |
140 |
650 |
Ф1000×3500 |
≤±5 |
-0.08 |
≤80 |
3000 |
6.0 |
|
ALM-250I |
250 |
650 |
Ф1000×5000 |
≤±5 |
-0.08 |
≤80 |
3500 |
7.5 |
Note: The technical parameters above are only for your reference. Finalized details are subject to final contract.
Alumall Material & Machine Co., Ltd is a professional vacuum varying pressure nitriding furnace manufacturer and supplier based in China. Over the past ten years of dedication, we are able to provide a wide array of high quality products, including aluminium billet heating furnace, aluminium melting furnace, hot top billet casting machine, dust collector for melting furnace, and more. Located in Foshan City, our company has access to convenient air, sea and land transportation. This guarantees lower transportation fees, reduces our production costs and saves customers on shipping charges. If you are interested in any of our furnaces, please feel free to contact us. The staff at Alumall Material & Machine Co., Ltd looks forward to working with you.
Alumall Material & Machine Co., Ltd
Add: 18#, Chuangye 1 Rd, Sanshui, Foshan, China
Tel: +86-757-87710953
Fax: +86-757-87719953
Mob: +86-13929943381/18144769953
Email: alumall@126.com
-
-
- Aging Furnace The aging furnace applies to the aging treatment for aluminum profiles to enhance product hardness and the mechanical performance... ...
-
-
-
- Homogenizing Furnace The homogenizing furnace is used to enhance the quality of aluminum profile products. Internal elements of aluminum billet (e.g. Mg2Si and Fe) will be uniform after treatment......
-
-
-
- Extrusion Die Heating Furnace The extrusion die heating furnace is used for heating and heat preservation for aluminum extrusion dies. The multi-chamber type die heating furnace is usually used to offer thorough heating and higher quality d...
-
-
-
- Single Billet Heating Furnace With Hot Log Shear The single billet heating furnace with hot log shear is used to recycle aluminum scrap to make new billet......
-